I picked this type of solder at the dollar store. Can i use this alloy to hold components to pcb?
On the wiki, it mentions it can hold radiator fins together. Which is usually copper or aluminum.
Am I correct that it has a wider temp range to solidify so it can cause broken joints more likely to form if not held steady?
On the wiki, it mentions it can hold radiator fins together. Which is usually copper or aluminum.
Am I correct that it has a wider temp range to solidify so it can cause broken joints more likely to form if not held steady?
Comment